Research on Dynamic Marine Atmospheric Corrosion Behavior of AZ31 Magnesium Alloy

doi:10.3390/met12111886

	Research on Dynamic Marine Atmospheric Corrosion Behavior of AZ31 Magnesium Alloy
	Wang, Ying1,2 ; Xu, Weichen 1,2; Wang, Xiutong 1,2; Jiang, Quantong 1,2; Li, Yantao 1,2; Huang, Yanliang 1,2; Yang, Lihui1,2
	2022-11-01
发表期刊	METALS
卷号	12 期号:11 页码:16
通讯作者	Yang, Lihui([email protected])
摘要	The dynamic marine atmospheric corrosion behavior of AZ31 magnesium alloy was investigated in situ exposed on the deck of marine scientific research vessel for 1 year. The marine scientific research vessel carried out five voyages from the coast of China to the western Pacific Ocean, while the navigation track and environmental data were collected and analyzed. The corrosion rate and characteristics were evaluated by using weight loss tests, scanning electron microscopy (SEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and electrochemical measurements. The corrosion rate from weight loss values was 52.23 mu m center dot y(-1) after exposure for 1 year, which was several times higher than that of the static field exposure test in marine atmospheric environment of other reported literature. The main corrosion products were Mg-5(CO3)(4)(OH)(2)center dot 4H(2)O, MgCO3 center dot 3H(2)O and Mg-2(OH)(3)Cl center dot 4H(2)O. The corrosion was initiated from pitting corrosion and evolved into general corrosion gradually. The serious corrosion maybe due to the harsh corrosive environment with alternating changes in temperature and relative humidity caused by multiple longitude and latitude changes, and particularly high deposition rate of chloride during voyage, which was nearly twenty times that on the coast of China. This study provides effective data for the application of magnesium alloy in shipboard aircraft and other equipment, and provides a reference for indoor simulation experiments.
关键词	magnesium alloy dynamic marine atmospheric corrosion ocean voyage
DOI	10.3390/met12111886
收录类别	SCI
语种	英语
资助项目	National Science and Technology Resources Investigation Program of China[2019FY101400]; Overseas Science and education cooperation center deployment project[121311KYSB20210005]; Wenhai Program of the S&T Fund of Shandong Province for Pilot National Laboratory for Marine Science and Technology (Qingdao)[2021WHZZB2304]
WOS研究方向	Materials Science ; Metallurgy & Metallurgical Engineering
WOS类目	Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
WOS记录号	WOS:000883625000001
出版者	MDPI
引用统计	被引频次：10[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.qdio.ac.cn/handle/337002/180357
专题	海洋环境腐蚀与生物污损重点实验室
通讯作者	Yang, Lihui
作者单位	1.Chinese Acad Sci, Inst Oceanol, Key Lab Marine Environm Corros & Biofouling, Qingdao 266071, Peoples R China 2.Pilot Natl Lab Marine Sci & Technol Qingdao, Open Studio Marine Corros & Protect, Qingdao 266237, Peoples R China
推荐引用方式 GB/T 7714	Wang, Ying,Xu, Weichen,Wang, Xiutong,et al. Research on Dynamic Marine Atmospheric Corrosion Behavior of AZ31 Magnesium Alloy[J]. METALS,2022,12(11):16.
APA	Wang, Ying.,Xu, Weichen.,Wang, Xiutong.,Jiang, Quantong.,Li, Yantao.,...&Yang, Lihui.(2022).Research on Dynamic Marine Atmospheric Corrosion Behavior of AZ31 Magnesium Alloy.METALS,12(11),16.
MLA	Wang, Ying,et al."Research on Dynamic Marine Atmospheric Corrosion Behavior of AZ31 Magnesium Alloy".METALS 12.11(2022):16.

条目包含的文件
文件名称/大小	文献类型	版本类型	开放类型	使用许可
metals-12-01886-v2.p（8582KB）	期刊论文	出版稿	限制开放	CC BY-NC-SA	浏览