Hydrogen Permeation Behavior of Carbon Steel During Corrosion in Highly Pressed Saturated Bentonite

doi:10.3389/fmats.2022.848123

	Hydrogen Permeation Behavior of Carbon Steel During Corrosion in Highly Pressed Saturated Bentonite
	Zhang, Qichao 1,2; Jiang, Yishan 2; Zhao, Xin 2; Song, Penglei 2; Kuang, Tingting 1; Chen, Juna 2; Sun, Zhongtao 2; Zhang, Yaopeng 2; Ai, Xiayu 2; Lu, Dongzhu 1; Huang, Yanliang 1
	2022-03-21
发表期刊	FRONTIERS IN MATERIALS
ISSN	2296-8016
卷号	9 页码:11
通讯作者	Lu, Dongzhu([email protected]) ; Huang, Yanliang([email protected])
摘要	Deep geological disposal is the most reliable method for high-level nuclear waste, of which metal container as the first barrier for deep geological disposal of high-level nuclear waste is particularly important. Carbon steel is used as a container material because of the low possibility of local corrosion in bentonite. However, after the storage is closed, the decrease of oxygen content will create a near-field environment where the hydrogen embrittlement (HE) in the corrosion process of the container could happen. To evaluate the safety of containers in deep geological disposal of Beshai, the preselected area in China, hydrogen permeation efficiency and HE were estimated in highly pressed saturated bentonite by electrochemical and extrapolation analyses. It is concluded that hydrogen permeation efficiency increases with the disposal year, which proves that the hydrogen evolution reaction dominates the cathode process in the corrosion during long-term disposal. However, slow strain rate tensile shows that Q235 steel has a low HE sensitivity.
关键词	hydrogen embrittlement metal corrosion hydrogen permeation bentonite nuclear waste
DOI	10.3389/fmats.2022.848123
收录类别	SCI
语种	英语
资助项目	National Natural Science Foundation of China[51471160]
WOS研究方向	Materials Science
WOS类目	Materials Science, Multidisciplinary
WOS记录号	WOS:000779125000001
出版者	FRONTIERS MEDIA SA
引用统计
文献类型	期刊论文
条目标识符	http://ir.qdio.ac.cn/handle/337002/178838
专题	海洋环境腐蚀与生物污损重点实验室
通讯作者	Lu, Dongzhu; Huang, Yanliang
作者单位	1.Chinese Acad Sci, Inst Oceanol, CAS Key Lab Marine Environm Corros & Biofouling, Qingdao, Peoples R China 2.Navy Submarine Acad, Qingdao, Peoples R China
第一作者单位	中国科学院海洋研究所
通讯作者单位	中国科学院海洋研究所
推荐引用方式 GB/T 7714	Zhang, Qichao,Jiang, Yishan,Zhao, Xin,et al. Hydrogen Permeation Behavior of Carbon Steel During Corrosion in Highly Pressed Saturated Bentonite[J]. FRONTIERS IN MATERIALS,2022,9:11.
APA	Zhang, Qichao.,Jiang, Yishan.,Zhao, Xin.,Song, Penglei.,Kuang, Tingting.,...&Huang, Yanliang.(2022).Hydrogen Permeation Behavior of Carbon Steel During Corrosion in Highly Pressed Saturated Bentonite.FRONTIERS IN MATERIALS,9,11.
MLA	Zhang, Qichao,et al."Hydrogen Permeation Behavior of Carbon Steel During Corrosion in Highly Pressed Saturated Bentonite".FRONTIERS IN MATERIALS 9(2022):11.

条目包含的文件
文件名称/大小	文献类型	版本类型	开放类型	使用许可
fmats-09-848123.pdf（2882KB）	期刊论文	出版稿	限制开放	CC BY-NC-SA	浏览