The corrosion behavior of EW75 magnesium alloy in the research vessel KEXUE during the ocean voyage

doi:10.1038/s41529-022-00238-0

	The corrosion behavior of EW75 magnesium alloy in the research vessel KEXUE during the ocean voyage
	Jiang, Quantong 1,2,3,4; Lu, Dongzhu 1,4; Cheng, Liren 2; Liu, Nazhen 1,4; Yang, Lihui1,4 ; Hou, Baorong 1,3,4
	2022-04-12
发表期刊	NPJ MATERIALS DEGRADATION
卷号	6 期号:1 页码:12
通讯作者	Jiang, Quantong([email protected])
摘要	The corrosion behavior of EW75 magnesium alloy in the Research Vessel KEXUE (RV KEXUE) during the ocean voyage was researched. The weight loss, corrosion depths, corrosion morphologies, and corrosion products were all analyzed. The mean weight loss rate of EW75 alloy Extrusion Surface was 0.0672 mg cm(-2) y(-1) (0.0903 mm y(-1)) after exposure corrosion tests, whereas that of Cross-section Surface was 0.0938 mg cm(-2) y(-1) (0.1537 mm y(-1)). Both extrusion direction and transverse direction of magnesium alloy samples occurred the brittle fracture in the harsh marine environment, and the mechanical strength fell precipitously after the exposure tests. The corrosion resistance of EW75 magnesium alloys obviously showed the anisotropy, which was due to the texture of the magnesium alloy in the microstructure. High salinity and high humidity environment led to a severe corrosion of EW75 magnesium alloys during exposure in the RV KEXUE during the ocean voyage. This study will provide the effective data for the service of magnesium alloys in typical marine atmospheric environment.
DOI	10.1038/s41529-022-00238-0
收录类别	SCI
语种	英语
资助项目	National Natural Science Foundation of China[41827805]; Open Funds of the State Key Laboratory of Rare Earth Resource Utilization[RERU2021017]; Hainan Province Science and Technology Special Fund[ZDYF2021GXJS210]
WOS研究方向	Materials Science
WOS类目	Materials Science, Multidisciplinary
WOS记录号	WOS:000781960300001
出版者	NATURE PORTFOLIO
引用统计	被引频次：6[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.qdio.ac.cn/handle/337002/178775
专题	海洋环境腐蚀与生物污损重点实验室
通讯作者	Jiang, Quantong
作者单位	1.Chinese Acad Sci, Inst Oceanol, CAS Key Lab Marine Environm Corros & Biofouling, 7 Nanhai Rd, Qingdao 266071, Peoples R China 2.Chinese Acad Sci, Changchun Inst Appl Chem, State Key Lab Rare Earth Resource Utilizat, 5625 Renmin St, Changchun 130022, Peoples R China 3.Chinese Acad Sci, Sanya Inst Oceanol, South China Sea Inst Oceanol, Zhenzhou Rd, Sanya 572000, Peoples R China 4.Pilot Natl Lab Marine Sci & Technol Qingdao, Open Studio Marine Corros & Protect, 1 Wenhai Rd, Qingdao 266235, Peoples R China
第一作者单位	中国科学院海洋研究所
通讯作者单位	中国科学院海洋研究所
推荐引用方式 GB/T 7714	Jiang, Quantong,Lu, Dongzhu,Cheng, Liren,et al. The corrosion behavior of EW75 magnesium alloy in the research vessel KEXUE during the ocean voyage[J]. NPJ MATERIALS DEGRADATION,2022,6(1):12.
APA	Jiang, Quantong,Lu, Dongzhu,Cheng, Liren,Liu, Nazhen,Yang, Lihui,&Hou, Baorong.(2022).The corrosion behavior of EW75 magnesium alloy in the research vessel KEXUE during the ocean voyage.NPJ MATERIALS DEGRADATION,6(1),12.
MLA	Jiang, Quantong,et al."The corrosion behavior of EW75 magnesium alloy in the research vessel KEXUE during the ocean voyage".NPJ MATERIALS DEGRADATION 6.1(2022):12.

条目包含的文件
文件名称/大小	文献类型	版本类型	开放类型	使用许可
s41529-022-00238-0.p（9038KB）	期刊论文	出版稿	限制开放	CC BY-NC-SA	浏览