Crack growth behaviour of E690 steel in artificial seawater with various pH values

doi:10.1016/j.corsci.2019.108336

	Crack growth behaviour of E690 steel in artificial seawater with various pH values
	Li, Yong 1; Liu, Zhiyong 1,2; Wu, Wei 1; Li, Xiaogang 1; Zhao, Jinbin 1,3
	2020-03-01
发表期刊	CORROSION SCIENCE
ISSN	0010-938X
卷号	164 页码:11
通讯作者	Liu, Zhiyong([email protected]) ; Li, Xiaogang([email protected])
摘要	In this study, the effect of artificial seawater pH value on crack growth behaviour of E690 steel was investigated. The results showed that the crack tip pH, which was determined by the electrical potential outside the crack, first increased and then decreased when the pH of artificial seawater decreased from 8.2-3.0. And, the crack growth rate was impacted by crack tip pH, first decreasing, then increasing with a decrease of the seawater pH; the lowest growth rate occurred at seawater pH 4.0. It revealed that the crack growth rate was fundamentally affected by the potential outside the crack.
关键词	Low alloy steel Acid solutions SEM Stress corrosion Crevice corrosion
DOI	10.1016/j.corsci.2019.108336
收录类别	SCI
语种	英语
资助项目	National Key R&D Program of China[2017YFB0304701]; Open Fund of Shandong Key Laboratory 'of Corrosion Science[KLCS201909]; National Natural Science Foundation of China[51771028]; National Natural Science Foundation of China[51601182]
WOS研究方向	Materials Science ; Metallurgy & Metallurgical Engineering
WOS类目	Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
WOS记录号	WOS:000515204200026
出版者	PERGAMON-ELSEVIER SCIENCE LTD
引用统计	被引频次：31[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://ir.qdio.ac.cn/handle/337002/165593
专题	海洋环境腐蚀与生物污损重点实验室
通讯作者	Liu, Zhiyong; Li, Xiaogang
作者单位	1.Univ Sci & Technol Beijing, Corros & Protect Ctr, Beijing 100083, Peoples R China 2.Chinese Acad Sci, Inst Oceanol, Shandong Key Lab Corros Sci, Qingdao 266071, Shandong, Peoples R China 3.Nanjing Iron & Steel United Co Ltd, Jiangsu Key Lab Premium Steel Mat, Nanjing 210035, Jiangsu, Peoples R China
通讯作者单位	中国科学院海洋研究所
推荐引用方式 GB/T 7714	Li, Yong,Liu, Zhiyong,Wu, Wei,et al. Crack growth behaviour of E690 steel in artificial seawater with various pH values[J]. CORROSION SCIENCE,2020,164:11.
APA	Li, Yong,Liu, Zhiyong,Wu, Wei,Li, Xiaogang,&Zhao, Jinbin.(2020).Crack growth behaviour of E690 steel in artificial seawater with various pH values.CORROSION SCIENCE,164,11.
MLA	Li, Yong,et al."Crack growth behaviour of E690 steel in artificial seawater with various pH values".CORROSION SCIENCE 164(2020):11.

条目包含的文件
文件名称/大小	文献类型	版本类型	开放类型	使用许可
1-s2.0-S0010938X1931（5907KB）	期刊论文	出版稿	限制开放	CC BY-NC-SA	浏览