	Investigation on role of corrosion generated hydrogen in process of stress corrosion cracking of austenitic stainless steel in marine atmospheric environment
	Huang, Y. L.; Dong, X. Q.; Chen, J.; Huang, YL (reprint author), Chinese Acad Sci, Inst Oceanol, Qingdao 266071, Peoples R China.
	2012-06-01
发表期刊	CORROSION ENGINEERING SCIENCE AND TECHNOLOGY
ISSN	1478-422X
卷号	47期号:4页码:284-288
文章类型	Article
摘要	Evidence on the role of corrosion generated hydrogen in stress corrosion cracking of austenitic stainless steel in marine atmospheric environment is provided. The formation of corrosive solution film on the surface of steel was observed. Hydrogen permeation through the stainless steel membrane was measured. Slow strain rate tests showed that anodic and cathodic polarisations around the free corrosion potential can both increase the elongation. Thermal desorption spectroscopy measurement showed hydrogen concentration increase under cathodic potentials. The hydrogen concentration increase under deformation conditions was also confirmed. However, hydrogen accumulation at the tip of the prenotched specimens was not detected.
关键词	Stainless Steel Hydrogen Permeation Stress Corrosion Cracking
学科领域	Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
DOI	10.1179/147842212X13342213397362
URL	查看原文
收录类别	SCI
语种	英语
WOS记录号	WOS:000304540000006
引用统计
文献类型	期刊论文
条目标识符	http://ir.qdio.ac.cn/handle/337002/12472
专题	海洋环境腐蚀与生物污损重点实验室
通讯作者	Huang, YL (reprint author), Chinese Acad Sci, Inst Oceanol, Qingdao 266071, Peoples R China.
作者单位	Chinese Acad Sci, Inst Oceanol, Qingdao 266071, Peoples R China
第一作者单位	中国科学院海洋研究所
推荐引用方式 GB/T 7714	Huang, Y. L.,Dong, X. Q.,Chen, J.,et al. Investigation on role of corrosion generated hydrogen in process of stress corrosion cracking of austenitic stainless steel in marine atmospheric environment[J]. CORROSION ENGINEERING SCIENCE AND TECHNOLOGY,2012,47(4):284-288.
APA	Huang, Y. L.,Dong, X. Q.,Chen, J.,&Huang, YL .(2012).Investigation on role of corrosion generated hydrogen in process of stress corrosion cracking of austenitic stainless steel in marine atmospheric environment.CORROSION ENGINEERING SCIENCE AND TECHNOLOGY,47(4),284-288.
MLA	Huang, Y. L.,et al."Investigation on role of corrosion generated hydrogen in process of stress corrosion cracking of austenitic stainless steel in marine atmospheric environment".CORROSION ENGINEERING SCIENCE AND TECHNOLOGY 47.4(2012):284-288.

条目包含的文件
文件名称/大小	文献类型	版本类型	开放类型	使用许可
Investigation on rol（679KB）			限制开放	使用许可	浏览

个性服务

推荐该条目

保存到收藏夹

查看访问统计

导出为Endnote文件

谷歌学术

谷歌学术中相似的文章

[Huang, Y. L.]的文章

[Dong, X. Q.]的文章

[Chen, J.]的文章

百度学术

百度学术中相似的文章

[Huang, Y. L.]的文章

[Dong, X. Q.]的文章

[Chen, J.]的文章

必应学术

必应学术中相似的文章

[Huang, Y. L.]的文章

[Dong, X. Q.]的文章

[Chen, J.]的文章

相关权益政策

暂无数据

收藏/分享

除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。